product description

A new generation of environmentally friendly waterborne coatings, pure water-based protective coatings, one-component, the main component is silicone acrylic emulsion.

Use

It is used for high-grade decorative painting of housing, public buildings, industrial building exterior walls and bridges.

Features

Free of organic solvents, non-toxic, non-polluting, non-flammable and non-explosive;

Dilute and clean the coating utensils with water, environmentally friendly coatings;

Excellent construction performance, the film has super weather resistance and color retention;

Scrub resistant, waterproof and mildew resistant, good anti-fouling performance;

Self-cleaning function to protect the substrate as new as ever;

Technical Parameters

1. Coating rate: single coating, theoretical value 10-12m2/kg, dry film thickness 30um, actual painting area will vary with different substrate conditions.

2. washable number: > 10,000 times.

3. Dilution ratio: Paint: water = 100:10-20 (weight ratio).

4. Recoating time: 4 hours later (25 ° C).

Best construction

1. Clean, dry and strong base.

2. Use cement putty to smooth the base surface.

3. Brush 1-2 times BA-30W waterborne epoxy primer.

4. use this product to dilute and mix thoroughly, brush 2-3 times, you can achieve the best results.

Technical requirements and surface treatment

The surface of the object to be coated should be thoroughly clean, clean and dry, free from foreign matter, and the concrete strength should be above C25. The wall has a moisture content of less than 15% and a pH of less than 10.

Construction Conditions

The ambient temperature is ≥10 °C, the humidity is ≤85%, and the surface temperature of the construction workpiece is greater than the dew point temperature of 3 °C.

Precautions

It is forbidden to work in rainy days or excessively humid weather to maintain the air circulation in the construction environment; excessive dilution of water will increase the risk of painting, and it is easy to produce problems such as insufficient hiding power and insufficient film film, which will eventually reduce the overall performance of the coating film. Too thick, it is recommended to have a dry film thickness of 30 μm.